HH-610S (1.6mm) hardfacing FCW welding wire for wear resistant layer
Charateristics
HH-610S produces a wear-resistant, austenitic, primary carbide-containing weld deposit. It is very resistant to abrasion.
Microstructure: High-chrome-high-carbon hard alloy on iron base with molybdenum additions C – Cr – Mo – Fe.
Machinability: Grinding only
Cutting: Not suited for flame-cutting
Cutting: Multi layers.
Application
Recommended particularly for the hardfacing of parts subjected to strong abrasion and medium impact stress, e.g. Vertical mill rollers, Mill discs, Roll presses, Sieves, Stirrer blades, Sand slingers and Top coats of Dredger teeth. The application temperatures should not exceed 500℃.
Typical compositions of pure welded deposit (3 layer welded )
| C | Cr | Mn | Si | Ni | Mo.V,Ti, Nb, others | ||||||||
| 3.5-4.2% | 23-28% | 0.5-1.0% | 0.7-1.2% | 0.1-0.25% | suitable | ||||||||
Hardness of pure welded deposit: ≥ 55 HRC
Package: 15 KG / Spool, 200 KG / drum, 100 KG / drum
Recommended welding parameters
Amperage [ A ] | Voltage [ V ] | Wire stick-out [ MM ] |
220-270 | 26-30 | 25~30 |
*This data sheet corresponds to the present state of production (August 2023) and can be changed anytime.