HH-700B Hardfacing FCW Welding Wire for CCO Wear Plate
High chromium wear-resistant plate flux cored wire, less welding spatter, smooth welded deposit smooth , high welding efficiency and high recovery rate.
Charateristics
HH-700B produces a wear-resistant, primary carbide-containing weld deposit. It is very resistant to abrasion.
Microstructure: High-chrome-high-carbon hard alloy on iron base: C – Cr – Fe.
Machinability: Grinding only
Cutting: Not suited for flame-cutting
Deposit thickness: 30 mm in Multil layers.
Application
Recommended particularly for the produce Chromium carbide overlay wear plate(CCO wear plate, or Bimetal plate) or wear resistant pipe, can also be used for hardfacing chutes, sieves, conveying channels, liners,hoppers.,etc. The application temperatures should not exceed 450℃.
Typical compositions of pure welded deposit (3 layer welded )
| C | Cr | Si | Mn | Ni,V,Ti, Mo, B,others | |||||||||||
| 4.8-5.5% | 23-28% | 0.7-1.5% | 0.6-1.0% | suitable | |||||||||||
Hardness of pure welded deposit: ≥ 60 HRC
Package: 250 KG / drum ,125 KG / drum
Recommended welding parameters
| Wire diameter [ MM ] | Amperage [ A ] | Voltage [ V ] | Wire stick-out [ MM ] | ||||||||||||
| 2.8 | 360-450 | 29-33 | 25-40 | ||||||||||||
*This data sheet corresponds to the present state of production (August 2023) and can be changed anytime.