HH-808s hardfacing FCW welding wire for Crusher
Charateristics
HH-808s is a high-performance flux cored welding wire, it produces an overlay resistant to abrasion and impact. The weld deposit cannot be machined. The weld material exhibits cracks。
Microstructure: High-chrome-high-carbon complex carbide alloy: C – Cr – Mo – V – Nb – Ni – Fe.
Machinability: Grinding only
Deposit thickness: Not suited for flame-cutting
Deposit thickness: Multi layers.
Application
Perfectly suited for parts subjected to combined impact and abrasive stresses, e.g. cone crushers, pick hammers, dredger teeth, crusher roll and guide rails. The application temperatures should not exceed 450℃.
Typical compositions of pure welded deposit (3 layer welded )
| C | Cr | Mn | Si | Mo、Nb、V、Ti、W、B+other | |||||||||
| 2.0-4.2% | 20-25% | 0.6-1.0% | 0.7-1.2% | 4.5-6.0% | |||||||||
Hardness of pure welded deposit: ≥ 50 HRC
Package: 15 kg / spool
Recommended welding parameters
Amperage [ A ] | Voltage [ V ] | Wire stick-out [ MM ] |
360-430 | 29~32 | 25~40 |
*This data sheet corresponds to the present state of production (August 2023) and can be changed anytime.